| Item | Unit | LSS-520MH | LSS-520MHB | LSS-
520MHF |
LSS-
520MHB-K |
LSS-
520MHF-K |
LSS-
540E |
Measurement Conditions |
| Appearance colour | - | Clear | Blue | Clear (Fluorescence by black light irradiation) | Blue | Clear (Fluorescence by black light irradiation) | Milky white | |
| Base | % | 25 | 25 | 25 | 15 | 15 | 40 | |
| Viscosity | mPa ·s | 400 | 400 | 400 | 40 | 40 | 12 | 25℃ |
| Young's modulus | MPa | 75 | 75 | 75 | 75 | 75 | 9.2 | Tensile speed 10mm/min |
| Elongation (23℃) | % | 460 | 460 | 460 | 460 | 460 | 500 | Tensile speed 300mm/min |
| Moisture vapor permeability | g/cm²-day | 0.002 | 0.002 | 0.002 | 0.002 | 0.002 | 0.0035 | 40℃ * 90%RH |
| Coating thickness:100µm | ||||||||
| Specific volume resistance | Ω·cm | 3.3 * 10^16 | 3.3 * 10^16 | 3.3 * 10^16 | 3.3 * 10^16 | 3.3 * 10^16 | 2.4 * 10^16 | JIS C2103 |
| Dry to touch | min. | 5 | 5 | 5 | 5 | 5 | 15 | Coating thickness:20µm |
Business Hours(Australia time)08:30-17:00 Except for Sat, Sun, and Holidays
About NITTO's SupportAdobe Reader is required to view PDF files.
If not yet installed, please download it from the Adobe website.
TEL +61-3-9213-1700
Business Hours(Australia time)08:30-17:00
Except for Sat, Sun, and Holidays