Black

Permanent PE laminate, parchment paper, or removable release liner

95% minimum by weight

Minimum 3 months @ 35°C

1.41 typical

6.5 - 9.0 mm

The noise reduction is a function of material mass per unit area. Material thickness should be set to provide desired sound transmission loss. Patches at 2 mm thick are widely used over sheet metal holes.

When subjected to a 90° peel at a rate of 300 mm/min on a

25 mm wide test specimen, the material has strength

>56.4 N (22.6 N/cm) after the following:

5 minute dwell

2 weeks

@ 70°C

2 weeks

@ 100% RH & 37.8°C

3 week environmental cycle

The material can be repositioned shortly after being applied (1-2 minutes)

and still meet above adhesion characteristics.

Withstands automotive bake cycles and maintains properties.

The material will show no evidence of sagging or pulling away from panel when a 34 g weight is attached to a 25 x 150 mm strip with the assembly hanging vertically for 24 hours.

No odor or mold development was evident after 2 weeks at

100% RH & 37.8°C.

The material will remain flexible and conformable at temperatures

as low as -30°C.

Meets FMVSS 302, self-extinguishing