Oxidation Polymerized Outdoor Anti-corrosion-corrosion Tape NITOHULLMAC™ XG Series

“Stick-on Corrosion Protection Paint!” Oxidation Polymerized Heavy Duty Anti-Corrosion Tape

The NITOHULLMAC XG Series is made of a plastic base nonwoven fabric impregnated with a compound which has a specially compounded drying oil as its main ingredient. Through oxidation polymerization, this compound forms a surface film which delivers outstanding corrosion and weather resistance. Since this material is extremely pliable, it only needs to be applied and smoothed down to adhere tightly to any location, regardless of the shape.This simple application forms an outstanding anti-corrosion and corrosion protection layer. *We recommend that NITOHULLMAC XG Series products be used together. This includes the anti-corrosion tape, under-coat material, filler material, and top coat material.

Installation Video
Features
Lineup
Applications
Download documents

Installation Video

See how NITOHULLMAC™ XG Series is installed.

Straight pipe Your browser does not support iframes	Frange Your browser does not support iframes
Elbow Your browser does not support iframes	Around a tank base Your browser does not support iframes

Features

Easy to apply, with remarkable workability

Extremely pliable, so it fits any complex shape precisely.
Application is accomplished simply by affixing, or wrapping, then smoothing it down.
Changes in viscosity due to low and high temperatures are minimal, and workability does not vary between summer and winter.

Gives outstanding anti-corrosion

The adhesive strength of this compound shuts out moisture and air from metallic surfaces.

Flame resistant

Conforms to criteria by Fire and Disaster Management Agency in Japan.

General Characteristics

Item	Units	NITOHULLMAC™ XG	Test Method
Thickness	µm	1100	AWWA C217-09
Weight	kg/m²	1.7	-
Tensile strength	N/m	6823	AWWA C217-09　/ ASTM D10000
Elongation	%	14	AWWA C217-09 / ASTM D10000
Water absorption ratio	%	0.5	24h water immersion
Insulation resistance	Ω・m²	3.0×10⁶	JIS Z 1902
Volume resistivity	Ω・cm	1.0×10¹¹	JIS K 6911
Adhesive strength	N/25mm	24	JIS Z 1902
Flame Resistance	-	Pass	Criteria by Fire and Disaster Management Agency in Japan
Heat resistance	℃	90	5 years' continuous use
Salt water spray	2,000h	No occurence of rust	JIS Z 1902
Weather Ability	2,000h	No occurence of rust	Sunshine Weatherometer
Drop melting point of saturant, (minimum)	℃	Over 100	AWWA C217-09 / ASTM D127

*The above values are sample observed values, not the guaranteed performance.

Salt Water Spray Test

			Test Method IOS Salt Water Spray Tester Test Time：2,000h Test Evaluation Appearance after Test： [Result]No occurrence of rust Appearance after peeling off the tape： [Result]No occurrence of rust
1.Appearance after 2,000 hours of the salt water spray test.	2.After peeling off the tape	3.After removing compound

Lineup

Category	Function	Product No.	Specification	Standard Quality Used	Featured, Applications
Main Material	Anti-corrosion Tapes	NITOHULLMAC™ XG	Thickness x Width x Length / Quantity 1.1㎜× 50mm×10m× 24Rolls/Case 1.1㎜×100mm×10m× 12Rolls/Case 1.1㎜×150mm×10m× 8Rolls/Case 1.1㎜×200mm×10m× 6Rolls/Case 1.1㎜×300mm×10m× 4Rolls/Case	-	Anti-corrosion tape for outdoor steel structures. A film is formed by oxidation polymerization Outstanding conformity to irregular shapes and weather resistance.
Supplementary Materials	Undercoat Materials	NITOHULLMAC™ XG-PN	Weight×Quantity 16kg×1Can/Case	300g/m²	Undercoat material which is effective in preventing corrosion of steel surfaces. This has the effect of improving the adhesion of tape.
	Undercoat Materials	NITOPRIMER AF	Weight×Quantity 14kg×10Can/Case	200g/m²	Undercoat material for use on concrete and mortar surfaces. This has the effect of improving the adhesion of tape.
	Filler Materials	NITOHULLMAC™ XG-M	Weight x Quantity 2kg x 10Pc / Case Thickness x Width x Length 25mm x 250mm x 200mm / 1Pc	-	For irregularly shaped parts such as flanges. A white clay consistency.
	Top Coat Materials	NITOHULLMAC™ XG-T	Weight x Quantity 4kg x 4Bags / Can / Case	300g /m²	Top coat material applied over the outdoor anti-corrosion tape. Forms a film in a short period of time and prevents the adhesion of dust, etc. Has the effect of heightening the tape's anti-corrosion and weather resistance.